Pinnacle PP 6135C3
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Pinnacle Polymers |
| Trademark: | Pinnacle PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BuMRDv_Pinnacle-PP-6135C3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
35 MELT FLOW CLARIFIED RANDOM COPOLYMER FOR INJECTION MOLDING Pinnacle Polymers Polypropylene 6135C3 is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties and lot-to-lot consistency. This product is intended for injection molding applications that require more stiffness, faster cycle time, low bloom, improved color, enhanced processability and excellent clarity. This product was produced using no organic peroxides. This product contains a new generation clarifier. The 6135C3 product provides:
Pinnacle's polypropylene, as marketed by Pinnacle Polymers Company, in natural, uncolored pellet form complies with appropriate requirements of CFR Title 21, Part 177, Subpart B, Section 177.1520 (c) 3.1a entitled "Olefin Polymers" of the Food Additives Amendment of 1958 to the United States Food, Drug and Cosmetic Act of 1938. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.6 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm, Injection Molded) | 29.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, 3.20 mm, Injection Molded) | 14 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(3.20 mm, Injection Molded) | 1140 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C, 3.20 mm, Injection Molded) | 53 | J/m | ASTM D256 |
| Notched Izod Impact (Area) 5(23°C, 3.20 mm, Injection Molded) | 5.20 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 79.0 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Haze (1270 µm) | 9.0 | % | |
| Yellowness Index | < -10 | YI |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 1.3 mm/min |
| 4 . | Type I |
| 5 . | Type I |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® 440 | Celanese Corporation | TPC-ET | Riteflex® |
| TAIRIPRO K3009AN | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| BESTNYL SI00VI02BEHX | Triesa Plastics | Nylon 6 | BESTNYL |
| ExxonMobil™ LDPE LD 157CW Wire & Cable | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Kinta FR3600A | Kinta Technology (Hong Kong) Co., Ltd. | ABS | Kinta |