Sindustris ABS LRS768
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bt9vef_Sindustris-ABS-LRS768.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LRS768 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for extrusion. Important attributes of Sindustris ABS LRS768 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 48.1 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 3.20 mm | > 5.0 | % | |
| Break, 3.20 mm | 35 | % | |
| Flexural Modulus 3(3.20 mm) | 2590 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 80.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 120 | J/m | |
| -30°C, 6.40 mm | 110 | J/m | |
| 23°C, 3.20 mm | 350 | J/m | |
| 23°C, 6.40 mm | 270 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 96.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 90.0 | °C | |
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Melt Temperature | 200 to 250 | °C | |
| Die Temperature | 200 to 250 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® TXG03 | A. Schulman Europe | ABS | RONFALIN® |
| SolVin 372NF | INOVYN | PVC, Unspecified | SolVin |
| YUNTIANHUA® M120 | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNTIANHUA® |
| Ultramid® SEG8 BK-126 | BASF Corporation | Nylon 6 | Ultramid® |
| Hifax EKC2038X | LyondellBasell Industries | PP Copolymer | Hifax |