Kalix® 2930 HFFR is a bio-sourced polyamide-based material specifically formulated to meet UL 94V2 @ 0.4 mm requirements for electronic devices. The material uses an advanced halogen-free flame retardant package expressly designed to minimize blooming, plate out, and other process related issues commonly associated with flame retardant materials. Black: Kalix® 2930 HFFR BK 000

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Good dimensional stability Low warpage Rigidity, high High strength Impact resistance, good Electroplateable Sprayable Fast molding cycle High liquidity Hot water formability Excellent appearance Flame retardancy
Uses	Thin wall parts Electrical/Electronic Applications Electrical components Mobile phone
RoHS Compliance	Contact manufacturer
Appearance	Black
Forms	Particle
Processing Method	Water temperature mold injection molding Injection molding
Part Marking Code (ISO 11469)	>PA610-GF30

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.41

Mechanical	Nominal Value	Unit	Test Method
Flexural Strain at Break	2.6	%	ISO 178

Additional Information	Nominal Value
UL Rating - V2 @ 0.4 mm

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage ¹			Internal method
Vertical flow direction	0.70	%	Internal method
Flow direction	0.20	%	Internal method
Water Absorption (23°C, 24 hr)	0.17	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	10600	MPa	ISO 527-2
Tensile Stress	130	MPa	ISO 527-2
Tensile Strain (Break)	2.4	%	ISO 527-2
Flexural Modulus	10000	MPa	ISO 178
Flexural Stress	200	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	9.0	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength	55	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	65.0	°C	DMA
Melting Temperature	223	°C

Additional Information	Nominal Value
Typical values shown tested on Dry as Molded samples. Standard Packaging and Labeling: Kalix® 2930 HFFR resin is packaged in foil lined, multiwall paper bags containing 25 kg (55 pounds) of material. Individual packages will be plainly marked with the product number, the color, the lot number, and the net weight.

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	4.0 - 12	hr
Suggested Max Moisture	< 0.090	%
Rear Temperature	265 - 275	°C
Front Temperature	280 - 295	°C
Processing (Melt) Temp	260 - 300	°C
Mold Temperature	80.0 - 120	°C

Injection instructions
Storage: Kalix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Kalix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Kalix® processing guide. Drying: Kalix® 2930 HFFR is supplied in sealed bags. It should be dried before molding because excessive moisture content will result in reduced mechanical properties and processing issues, such as excessive nozzle drooling, foaming and splay visible on the molded parts. Polyamides oxidize in the presence of oxygen at high temperatures. Therefore drying temperatures above 80°C (176°F) should be avoided, particularly for light colors or color-controlled parts. Injection Molding: Set injection pressure to give rapid injection. Adjust holding pressure to one-half injection pressure. Set hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled.

Injection instructions

Storage: Kalix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Kalix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Kalix® processing guide. Drying: Kalix® 2930 HFFR is supplied in sealed bags. It should be dried before molding because excessive moisture content will result in reduced mechanical properties and processing issues, such as excessive nozzle drooling, foaming and splay visible on the molded parts. Polyamides oxidize in the presence of oxygen at high temperatures. Therefore drying temperatures above 80°C (176°F) should be avoided, particularly for light colors or color-controlled parts. Injection Molding: Set injection pressure to give rapid injection. Adjust holding pressure to one-half injection pressure. Set hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled.

Note Message
1 .	Solvay Test Method. Shrink rates can vary with part design and processing conditions. Please consult a Solvay Technical Representative for more information.

Category:	HPPA , High Performance Polyamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Kalix®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Bt098G_Kalix-2930-HFFR.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TEKNIFLEX® VAV5605	Tekni-Films, a div of Tekni-Plex	Film, PVC/PCTFE/PVC	TEKNIFLEX®
UTEC 3040	Braskem	UHMWPE	UTEC
Formolene® 2510W	Formosa Plastics Corporation, U.S.A.	PP Impact Copolymer	Formolene®
Elexar® EL-8313R	Teknor Apex Company	TPE	Elexar®
Sylvin 4250-85 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin