TECHNYL® C 50H2 BLACK 46 N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BsoLLn_TECHNYLC50H2BLACK46N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® C 50H2 Black 46 N is an unfilled Non-phosphorous and Non-halogenated flame retardant polyamide 6, heat stabilized, for injection moulding. This product, UL94 VO @ 0,4mm, offers excellent moldability together with good stiffness. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3500 | 2000 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Yield, 23°C | 80.0 | -- | MPa | ASTM D638 |
| Yield, 23°C | 75.0 | 50.0 | MPa | ISO 527-2/1A |
| Fracture, 23°C | 80.0 | -- | MPa | ASTM D638 |
| Fracture, 23°C | 60.0 | 40.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ||||
| Yield, 23°C | 3.5 | 5.0 | % | ISO 527-2 |
| Fracture, 23°C | 15 | -- | % | ASTM D638 |
| Fracture, 23°C | 25 | 38 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 3500 | -- | MPa | ASTM D790 |
| 23°C | 3150 | 2000 | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 115 | -- | MPa | ASTM D790 |
| 23°C | 200 | 70.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 180 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 65 | -- | J/m | ASTM D256 |
| 23°C | 3.5 | 15 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 34 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.50 | 3.90 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.060 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution a | 600 | 600 | V | IEC 60112 |
| Solution B | 475 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | V-0 | -- | UL 94 | |
| 0.8 mm | V-0 | -- | UL 94 | |
| 1.6 mm | V-0 | -- | UL 94 | |
| 3.2 mm | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.8 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.6 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.2 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.8 mm | 700 | -- | °C | IEC 60695-2-13 |
| 1.6 mm | 700 | -- | °C | IEC 60695-2-13 |
| 3.2 mm | 700 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 36 | -- | % | ISO 4589-2 |
| French Fire Index | F2 | -- | NF F16-101 | |
| French Smoke Index | I2 | -- | NF F16-101 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| European Railways Certifications | EN 45545-2 | |||
| R22 | HL3 | -- | EN 45545-2 | |
| R23 | HL3 | -- | EN 45545-2 | |
| R25 | HL3 | -- | EN 45545-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 - 235 | °C | |
| Middle Temperature | 235 - 240 | °C | |
| Front Temperature | 235 - 245 | °C | |
| Mold Temperature | 60 - 90 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: All reinforced flame retardant compounds generate some level of abrasion/corrosion to the steel processing equipment. These issues can be worsened by using incorrect processing conditions (temperatures, residence time, moisture level ...) during the moulding process. Therefore, Solvay recommends to use the advised processing conditions detailed in this technical data sheet. For equipment that comes into contact with molten flame retarded compounds, Solvay advises to use a steel containing high chromium & high carbon content (minimum concentration of 16% Chromium) to prevent corrosion and abrasion. For the correct reference of steel associated to flame retardant compounds processing, please refer to your equipment manufacturers. For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature at 120°C. Of course it should be noted that this improvement in the surface appearance may be at the expense of the cycle time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® N 2640 E2 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| ZEONOR® 1060R | Zeon Corporation | COP | ZEONOR® |
| 4LEX® 9F22105 | 4Plas | PC | 4LEX® |
| Karina WHITE PVC COMP -E 847-10/189-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 7833-90 Brown 7108 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |