AKROMID® B3 2 RM-D natural (3390)
| Category: | Nylon 6+ABS , Polyamide 6 + ABS |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bsno8H_AKROMID-B3-2-RM-D-natural-3390-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 2 RM-D natural (3390) is a nonreinforced, UV-stabilised polyamide 6 with limited moisture absorption and light inherent colour Applications are interior and exterior parts with improved impact strength in the automotive industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.08 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 62.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.80 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.6 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2300 | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 50.0 | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 3.3 | 15 | % | |
| Break | > 40 | > 100 | % | |
| Flexural Modulus 1 | 2200 | -- | MPa | ISO 178 |
| Flexural Stress | 70.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 16 | kJ/m² | |
| 23°C | 20 | 65 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 2 | 225 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10 K/min, DSC |
| 3 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKASUPER® LCP E5002L | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Huafon T26 | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| Plasmer 2080B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| Sylvin 802-88 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 5224-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |