Sarlink® TPE ME-2380B BLK
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BsXEFZ_SarlinkTPEME2380BBLK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ME-2300B is high performance TPE designed for automotive exterior application with good UV resistance and good flow properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 3.70 | MPa | ASTM D412 |
| 300% strain | 4.90 | MPa | ASTM D412 |
| Tensile Strength (Break) | 12.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 760 | % | ASTM D412 |
| Compression Set (70°C, 22 hr) | 66 | % | ASTM D395 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 157 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35 - 66 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 42 T 13-8 | Ravago Group | PP Homopolymer | Scolefin |
| Sicoklar E51.20 | Ravago Group | PC | Sicoklar |
| Sylvin 8692-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nanguang TPU S-72DX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| ADLAS® O07FFB-00 | A.D. Compound S.p.A. | PP Homopolymer | ADLAS® |