TEKAMID™ TA631
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BsS1bc_TEKAMID-TA631.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TA631 is GF/CF 30% reinforced Polyamide66. TA631 has good properties with 10^4 ohm surface electric resistivity. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 186 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3 | 11800 | MPa | ASTM D790 |
| Flexural Strength 4 | 284 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 250 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 235 | °C | ASTM D648 |
| Peak Melting Temperature | 255 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 295 | °C | |
| Front Temperature | 285 - 295 | °C | |
| Nozzle Temperature | 285 - 295 | °C | |
| Processing (Melt) Temp | 285 - 295 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Injection Speed: 40 to 70%Injection Pressure - 1st: 20 to 50%Injection Pressure - 2nd: 20 to 50%Injection Pressure - Back Pressure: 0 to 20% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texalan® 5 Series 572D | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 5 Series |
| Bergamid™ BG6000-8034 RS NC001 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| BJB Polyurethane SC-92 | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| FHR Polypropylene P4G3Z-050 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Hostacom TRC 352N E3 G62514 | LyondellBasell Industries | PP Copolymer | Hostacom |