Resirene 2210
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Resirene, S.A. de C.V. |
| Trademark: | Resirene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Br2L6U_Resirene-2210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Resirene 2210 is a HIPS grade suitable for injection molding processes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 16 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1730 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 16.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 43 | % | ASTM D638 |
| Flexural Modulus | 1700 | MPa | ASTM D790 |
| Flexural Strength | 26.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 3.18 mm | 96 | J/m | |
| 12.7 mm | 85 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 69.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 78.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| GELAST GT70ISB | Guang Sung Plastics (GSPL) | SEBS | GELAST |
| Elastron® G G500.A80.B.ABS | Elastron USA, Inc. | SEBS | Elastron® G |
| Keyflex® BT 2140D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| Mafill® CR CME 5144 | Ravago Group | PP Copolymer | Mafill® |
| PLUSTEK PA320G4 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |