Adstif EA648P
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adstif |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BqsKTu_Adstif-EA648P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adstif EA648P is a high crystalline impact copolymer with outstanding mechanical properties. The product features an easy processability, an excellent combination of stiffness and impact resistance and good gloss. Adstif EA648P is a single component solution for high stiffness injection moulding applications to replace mineral filled compounds with polymer blends. This grade is suitable for a wide range of appliances in the rigid packaging and consumer goods industries, such as housings for electrical appliances, furniture and technical components. Adstif EA648P is UL listed under file E31765. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 25.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 71.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.5 | kJ/m² | |
| 0°C | 3.0 | kJ/m² | |
| 23°C | 5.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 60 | kJ/m² | |
| 0°C | 85 | kJ/m² | |
| 23°C | 140 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/B |
| Ductile / Brittle Transition Temperature | -40.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A50 |
| -- | 84.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 70 | ASTM D2457 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP5078 | PolyMirae | PP Copolymer | Moplen |
| Nipol® NBR DN302 | Zeon Corporation | NBR | Nipol® NBR |
| ELASTOSIL® R plus 4305/40 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| LUMISIL® 868 | Wacker Chemie AG | Silicone | LUMISIL® |
| XENOY™ 1760E resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |