Devcon Combo Wear FC
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bqou9n_Devcon-Combo-Wear-FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High-tech, epoxy compound for quickly repairing processing equipment and returning to service in as little as 1.5 hours Intended Use:
Product features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.20 | g/cm³ | |
| Specific Volume | 0.448 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Resistance | |||
| Dry | 149 | °C | |
| Wet | 60 | °C | |
| Tensile Shear Adhesion | 10.0 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.080 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 29.6 | MPa | ASTM D638 |
| Flexural Strength | 49.2 | MPa | ASTM D790 |
| Compressive Strength | 75.8 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 6.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant | 41.0 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 2.0 Mixing ratio by capacity: 2.0 | ||
| Component B | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Pot Life (24°C) | 7.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 8.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-IM-G40 | Polymer Resources Ltd. | Nylon 66 | PRL |
| Reny® 2041 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Radilon® S BMX200K 333 NER | Radici Plastics | Nylon 6 | Radilon® |
| Durez® 118 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Karina CLEAR PVC COMPOUND 80/315-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |