DOW™ LDPE 401C
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BqZU0Q_DOW-LDPE-401C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW™ LDPE 401C is a Low Density Polyethylene Resin material. It is available in Latin America. Typical application of DOW™ LDPE 401C: Food Contact Applications |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 12.0 | MPa | |
| TD : Yield, 38 µm | 12.0 | MPa | |
| MD : Break, 38 µm | 25.0 | MPa | |
| TD : Break, 38 µm | 20.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm | 300 | % | |
| TD : Break, 38 µm | 600 | % | |
| Dart Drop Impact (38 µm) | 130 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 340 | g | |
| TD : 38 µm | 100 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm) | 40 | ASTM D2457 | |
| Haze (38.0 µm) | 14 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Durez® 22257 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| LUVOCOM® 21-8115 | Lehmann & Voss & Co. | Nylon 6/6T | LUVOCOM® |
| Lustran® ABS 786 | Styrolution | ABS | Lustran® ABS |
| OTECH PVC OE8536 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Moplen HP648H | LyondellBasell Industries | PP Homopolymer | Moplen |