Lupoy® GN5151RFA
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bop1hL_Lupoy-GN5151RFA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, High Stiffness, Halogen Free Flame Retardent Application IT/OA(Notebook PC Housing) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 66.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 20 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 4410 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 113 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 95.0 | °C | ASTM D648 |
| RTI Elec (1.00 to 1.10 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.00 to 1.10 mm) | 60.0 | °C | UL 746 |
| RTI Str (1.00 to 1.10 mm) | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 245 to 265 | °C | |
| Front Temperature | 260 to 275 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Processing (Melt) Temp | 245 to 275 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 0.981 to 1.96 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A12^ F30 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Terlux® BX13010 | INEOS Styrolution Group GmbH | MABS | Terlux® |
| Baoding 76E80 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| Cheng Yu A705G3 | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| DIOSHY® TPEE E955D-HD | DIOSHY Co.,Ltd. | TPEE | DIOSHY® |