Sarlink® TPV X17180B
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BnwKK7_Sarlink-TPV-X17180B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Sarlink 17100 Series are super high flow injection molding grades with excellent UV resistance for exterior applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.913 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 5 sec | 82 | ||
| Shore A, 15 sec | 80 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Across Flow : 100% Strain | 3.13 | MPa | |
| Flow : 100% Strain | 3.50 | MPa | |
| Tensile Strength | ISO 37 | ||
| Across Flow : Break | 5.40 | MPa | |
| Flow : Break | 5.50 | MPa | |
| Tensile Elongation | ISO 37 | ||
| Across Flow : Break | 460 | % | |
| Flow : Break | 400 | % | |
| Tear Strength 1 | ISO 34-1 | ||
| Across Flow | 28 | kN/m | |
| Flow | 27 | kN/m | |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 31 | % | |
| 70°C, 22 hr | 43 | % | |
| 125°C, 70 hr | 64 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow (150°C, 168 hr) | -14 | % | ISO 37 |
| Change in Tensile Modulus in Air - Across Flow (150°C, 168 hr) | 4.3 | % | ISO 37 |
| Change in Ultimate Elongation in Air - Across Flow (150°C, 168 hr) | -27 | % | ISO 37 |
| Change in Shore Hardness in Air | ISO 868 | ||
| Shore A, 150°C, 168 hr 2 | 2.4 | ||
| Shore A, 150°C, 168 hr 3 | 1.8 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, 206 1/s (200°C) | 188 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 205 | °C | |
| Middle Temperature | 180 to 205 | °C | |
| Front Temperature | 180 to 205 | °C | |
| Nozzle Temperature | 185 to 210 | °C | |
| Processing (Melt) Temp | 185 to 210 | °C | |
| Mold Temperature | 10.0 to 55.0 | °C | |
| Back Pressure | 0.100 to 1.00 | MPa | |
| Screw Speed | 100 to 200 | rpm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| 2 . | 15 sec delay |
| 3 . | 5 sec delay |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP212V0 | Kolon Plastics, Inc. | PBT | SPESIN® |
| BP Flex A 6310 BLK | Buckeye Polymers, Inc. | TPE | BP Flex |
| Arnitel® VT3104 | DSM Engineering Plastics | TPE | Arnitel® |
| GLS PP ZT89 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| Plenco 08122 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |