TOTAL Polystyrene Impact 3450
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bm1QLD_TOTAL-Polystyrene-Impact-3450.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYSTYRENE IMPACT 3450 is a high impact polystyrene with high heat resistance, good flow, high stiffness and good aesthetics. With such an ideal balance of properties, POLYSTYRENE IMPACT 3450 is well suited for the fabrication of heat resistant items by injection molding and extrusion-thermoforming. In injection molding, the combination of good flow and high heat resistance of POLYSTYRENE IMPACT 3450 makes short cycle times possible. In extrusion-thermoforming, POLYSTYRENE IMPACT 3450 is perfectly designed for hot-fill applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 77 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2250 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 32.5 | MPa | |
| Break | 28.0 | MPa | |
| Tensile Strain (Break) | 55 | % | ISO 527-2 |
| Flexural Modulus | 2250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 77.0 | °C | |
| 1.8 MPa, Annealed | 94.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ISO 306/A50 |
| -- | 95.0 | °C | ISO 306/B50 |
| CLTE - Flow | 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Electric Strength | 150 | kV/mm | IEC 60243-1 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 80 | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 30 FR 2 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| ASI POLYPROPYLENE 1500X-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| HiFill® MD POM 0167 LE | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| HYBRANCH HP-500M | DIC Corporation | PS (Specialty) | HYBRANCH |
| OmniTech™ PBT FR GF30 | OMNI Plastics, LLC | PBT | OmniTech™ |