Lucalen A 2540 D
| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lucalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BlokP7_Lucalen-A-2540-D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucalen A 2540 D is a low density Polyethylene, containing comonomer. It is delivered in pellet form. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ISO 1133 |
| n-Butyl Acrylate Content | 6.5 | wt% | DIN 51451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 120 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 7.00 | MPa | ISO 527-2 |
| Coefficient of Friction | > 0.80 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 2.4-8.7 mil (60-220 µ) | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, blown film | 26.0 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 350 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 550 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 600 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 86.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 103 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | > 20 | ASTM D2457 | |
| 60, 50.0 µm, blown film | > 70 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 13 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Failure Energy (70.0 µm) | 190 | J/cm | DIN 53373 |
| Film properties tested using 50 µm thickness blown film extruded at a melt temperature of 200°C and a blow-up ratio of 2:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 885 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| SILVER® ABS 313NM | Guangdong Silver Age Sci & Tech. Co., Ltd | ABS | SILVER® |
| Abstron AN450N | Bhansali Engineering Polymers Limited | ABS | Abstron |
| LNP™ STAT-KON™ EX11402 compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| SD POLYCA™ 875G20F | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |