INELEC PCABSCF10
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INELEC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BlSBHz_INELEC-PCABSCF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INELEC PCABSCF10 is a Polycarbonate + ABS (PC+ABS) product filled with 10% carbon fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 112 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 7240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact | 320 to 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 129 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 246 to 266 | °C | |
| Mold Temperature | 51.7 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.051 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKASTER™ F100 | Mando Advanced Materials Co., Ltd. | PBT | TEKASTER™ |
| Network Polymers LDPE 10 0127 EVA | Network Polymers, Inc. | EVA | Network Polymers LDPE |
| Hyundai EP PA6 LS130 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| LEXAN™ PC0700 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LNP™ THERMOTUF™ DF004PSI compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOTUF™ |