Honeywell Halar E500
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | Honeywell Halar |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BlMtGX_Honeywell-Halar-E500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Honeywell Halar® E-Series ECTFE film is a high performance film with excellent mechanical, electrical and release properties. It is non-flammable, and has outstanding chemical resistance. Halar E-Series Film is available in the following colors: Blue, White and Clear. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.28 | ASTM D1894 | |
| With self-dynamics | 0.58 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD | 1930 | MPa | ASTM D882 |
| TD | 1520 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 35.2 | MPa | ASTM D882 |
| TD : Yield | 31.0 | MPa | ASTM D882 |
| MD : Fracture | 83.8 | MPa | ASTM D882 |
| TD : Fracture | 57.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 180 | % | ASTM D882 |
| TD : Fracture | 280 | % | ASTM D882 |
| Water Vapor Transmission Rate (38°C, 100% RH) | 0.20 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 240 | °C | ASTM D3418 |
| Additional Information |
|---|
| Yield: 32980 in²/lbTensile Strength @ Yield, ASTM D 882, MD: 4500 to 5700 psiTensile Strength @ Yield, ASTM D 882, TD: 4000 to 5000 psiTensile Strength @ Break, ASTM D 882, MD: 88000 to 15500 psiTensile Strength @ Break, ASTM D 882, TD: 6200 to 10500 psiElongation @ Break, ASTM 882, MD: 90 to 275%Elongation @ Break, ASTM 882, TD: 210 to 355%Secant Modulus, ASTM D 882, MD: 230000 to 330000 psiSecant Modulus, ASTM D 882, TD: 190000 to 250000 psiGraves Tear (initial), ASTM D 1004, MD: 400 to 570 g/milGraves Tear (initial), ASTM D 1004, TD: 350 to 2700 g/milDimensional Stability, ASTM D1204, 300°F, 10 min: <3% shrinkageCoef of Friction, ASTM D1894, Vs Metal - Dynamic: 0.23 to 0.33Coef of Friction, ASTM D1894, Vs Itself - Dynamic: 0.30 to 0.86 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 T20 G10 NTAL010 NR460 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Altuglas® BS 520 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Amilan® CM1011G-30 | Toray Resin Company | Nylon 6 | Amilan® |
| Asaprene™ T-432 | AKelastomers | SBS | Asaprene™ |
| Forprene® 6NM001A70 | SO.F.TER. SPA | TPV | Forprene® |