POLYFORT® FPP 3363
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BkgotQ_POLYFORT-FPP-3363.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP 10% Glass Fiber Chemically Coupled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 0.36 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 50.0 | MPa | ASTM D638 |
| Flexural Modulus 3 | 2200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 152 | °C | |
| 1.8 MPa, Unannealed | 118 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 10 | % | ASTM D5630 |
| Note Message | |
|---|---|
| 1 . | 5x7 in plaque |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® PJ9300C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Styrolution PS 1611 | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| ColorRx® PCT-1500RX | LTL Color Compounders, Inc. | PC+PET | ColorRx® |
| FORMULA P COMP 6220 M1 Z | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Lionpol HF-204567 | Lion Polymers Incorporated | TPE | Lionpol |