Hyflon® F is a unique new family of MFA polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame resistance, low surface energy and exceptional dielectric properties. Hyflon® MFA F1520 is a low melt flow rate multi purpose resin with an exceptional stress crack resistance, continuous service temperature up to 225°C and a 100-150x10³ cycles flex-life (on a 0.3mm flim, ASTM D2176).

General Information
Features	High ESCR (Stress Cracking Resistance) Good flexibility Low liquidity Flame retardancy
Uses	Wire and cable applications General
RoHS Compliance	RoHS compliance
Forms	Particle
Processing Method	Extrusion coating

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.10 - 2.15	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (372°C/5.0 kg)	1.0 - 4.0	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	55 - 60		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹(23°C)	400 - 500	MPa	ASTM D3307
Tensile Strength ²(Break, 23°C)	> 30.0	MPa	ASTM D3307
Tensile Elongation ³(Break, 23°C)	> 300	%	ASTM D3307
Bending life ⁴	1.0E+5 - 1.5E+5	Cycles	ASTM D2176

Thermal	Nominal Value	Unit	Test Method
Heat of crystallization	16.0 - 24.0	J/g	DSC
Heat of Fusion	16.0 - 24.0	J/g	DSC

Extrusion	Nominal Value	Unit
Flange temperature	370 - 400	°C

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	No Break

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	265 - 275	°C	ASTM D3307
Peak Crystallization Temperature (DSC)	255 - 265	°C	DSC
CLTE - Flow	1.2E-4 - 2.0E-4	cm/cm/°C	ASTM D696
Specific Heat (23°C)	900 - 1100	J/kg/°C	DSC
Thermal Conductivity (40°C)	0.20	W/m/K	ASTM C177

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+17	ohms	ASTM D257
Volume Resistivity	> 1.0E+17	ohms·cm	ASTM D257
Dielectric Strength ⁵(1.00 mm)	35 - 40	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
23°C, 50 Hz	2.00		ASTM D150
23°C, 100 kHz	2.00		ASTM D150
Dissipation Factor			ASTM D150
23°C, 50 Hz	< 5.0E-4		ASTM D150
23°C, 100 kHz	< 5.0E-4		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating	V-0		UL 94
Oxygen Index	95	%	ASTM D2863

Additional Information
COLOR MASTER BATCHES We recommend that only Color Master Batches based in Hyflon MFA be used. Master Batches based on other fluoropolymers can negatively influence the superior processing and electrical performance of the resin. A list of suppliers can be obtained from your Solvay sales representative. HEALTH SAFETY AND ENVIRONMENT Hyflon MFA F1520 is a very inert polymer and it is not harmful if used and handled according to standard processing procedures. If handled inappropriately, it may release harmful toxic chemicals. Hyflon MFA F1520 does not contain any RoHS or WEEE substances. Hyflon MFA F1520 is not produced using APFO and contains no APFO. Please refer to the Material Safety Data Sheets for more information on handling and safety. PACKAGING AND STORAGE Hyflon MFA F1520 resin is available in 25 kg (55 lbs) and 500 kg (1102 lbs) packaging. Though it has an indefinite shelf life, it is recommended to store it in a clean area, protected by direct sun light and possible contamination.

Additional Information

COLOR MASTER BATCHES We recommend that only Color Master Batches based in Hyflon MFA be used. Master Batches based on other fluoropolymers can negatively influence the superior processing and electrical performance of the resin. A list of suppliers can be obtained from your Solvay sales representative. HEALTH SAFETY AND ENVIRONMENT Hyflon MFA F1520 is a very inert polymer and it is not harmful if used and handled according to standard processing procedures. If handled inappropriately, it may release harmful toxic chemicals. Hyflon MFA F1520 does not contain any RoHS or WEEE substances. Hyflon MFA F1520 is not produced using APFO and contains no APFO. Please refer to the Material Safety Data Sheets for more information on handling and safety. PACKAGING AND STORAGE Hyflon MFA F1520 resin is available in 25 kg (55 lbs) and 500 kg (1102 lbs) packaging. Though it has an indefinite shelf life, it is recommended to store it in a clean area, protected by direct sun light and possible contamination.

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	240 - 290	°C
Cylinder Zone 2 Temp.	270 - 320	°C
Cylinder Zone 3 Temp.	300 - 360	°C
Cylinder Zone 4 Temp.	320 - 380	°C
Cylinder Zone 5 Temp.	340 - 390	°C
Adapter Temperature	370 - 400	°C
Melt Temperature	400	°C
Die Temperature	390 - 420	°C

Extrusion instructions
EXTRUSION PROCESSING GUIDELINES As with other fluoropolymers, Hyflon MFA is corrosive in the melt. Therefore all parts coming into prolonged contact with the melt should be made with corrosion resistant materials such as Hastelloy®, Inconel®, Monel® or Xaloy®. Chrome or nickel plating is not recommended since they are typically only sufficient for brief processing tests. F1520 is suitable for extrusion using techniques normally applied for other thermo-processable plastics, provided that the extruder is equipped with corrosion resistant alloys. Extruders with L/D ratio of 20:1 to 30:1 are recommended. Extruders should be equipped with independently controlled heaters capable of accurate temperature control up to 450°C (840°F). An overview of the temperature, tooling and equipment requirements are in the following tables. Many different screw designs can be used. Single-flight screws are recommended while barrier-flights should be avoided. A typical screw design consist of a long feed section (at least 12 flights), followed by a 2 to 6 flight transition and a 5 to 7 flight metering section.

Extrusion instructions

EXTRUSION PROCESSING GUIDELINES As with other fluoropolymers, Hyflon MFA is corrosive in the melt. Therefore all parts coming into prolonged contact with the melt should be made with corrosion resistant materials such as Hastelloy®, Inconel®, Monel® or Xaloy®. Chrome or nickel plating is not recommended since they are typically only sufficient for brief processing tests. F1520 is suitable for extrusion using techniques normally applied for other thermo-processable plastics, provided that the extruder is equipped with corrosion resistant alloys. Extruders with L/D ratio of 20:1 to 30:1 are recommended. Extruders should be equipped with independently controlled heaters capable of accurate temperature control up to 450°C (840°F). An overview of the temperature, tooling and equipment requirements are in the following tables. Many different screw designs can be used. Single-flight screws are recommended while barrier-flights should be avoided. A typical screw design consist of a long feed section (at least 12 flights), followed by a 2 to 6 flight transition and a 5 to 7 flight metering section.

Note Message
1 .	1.0 mm/min
2 .	50 mm/min
3 .	50 mm/min
4 .	0.3mm film
5 .	50Hz

Category:	Perfluoropolymer , Perfluoropolymer
Manufacturer:	Solvay Specialty Polymers
Trademark:	Hyflon® MFA®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	BkOnX7_Hyflon-MFA-F1520.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TABOND 3032	SILON s.ro	LDPE+LLDPE	TABOND
Sylvin 8739-70FU Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Braskem PP TI2600C	Braskem America Inc.	PP, High Crystal	Braskem PP
Geon™ Vinyl Flexible B70CB	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
Electrafil® TPU 95A CF15	Techmer Engineered Solutions	TPU, Unspecified	Electrafil®