LONGLITE® PMC T200NA
| Category: | Phenolic , Phenolic |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BkHQyx_LONGLITE-PMC-T200NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PMC-T200NA Black Phenolic is a one-stage, ammonia free molding material offering excellent mold process-ability and optimized Cure cycles. Typical applications include, transformer part, electrical insulation applications, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, JIS K7112 |
| Molding Shrinkage | 1.0 | % | JIS K6915, ASTM D955 |
| Water Absorption | |||
| 24 hr | 0.30 | % | ASTM D570 |
| 23°C, 24 hr | 0.30 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 60.0 | MPa | ASTM D638, JIS K6911 |
| Flexural Strength | 95.0 | MPa | ASTM D790, JIS K7203 |
| Compressive Strength | 200 | MPa | ASTM D695, JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Impact Strength | |||
| -- | 3.4 | kN/m | ASTM D256 |
| -- | 3.4 | kN/m | JIS K7111 |
| Izod Impact | |||
| -- | 2.9 | kN/m | ASTM D256 |
| -- | 2.9 | kN/m | JIS K6911 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life | 6 | month |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 180 | °C | ASTM D648, JIS K7207 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI Str | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+12 | ohms·cm | ASTM D257, JIS K6911 |
| Dielectric Strength | 12 | kV/mm | ASTM D149, JIS K6915 |
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Insulation Resistance | |||
| -- 1 | 1.0E+10 | ohms | ASTM D257 |
| -- 2 | 1.0E+10 | ohms | JIS K6915 |
| -- 3 | 1.0E+8 | ohms | ASTM D257 |
| -- 4 | 1.0E+8 | ohms | JIS K6915 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.380 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | (N) |
| 2 . | (N) |
| 3 . | (B) |
| 4 . | (B) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax RP320N | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| RAMTOUGH RZ720 | Polyram Ram-On Industries | PC | RAMTOUGH |
| ZELAS® MC721AP | Mitsubishi Chemical Performance Polymers, Inc. | TPE | ZELAS® |
| FERREX® GPP30CC65HB BLACK | Ferro Corporation | PP Homopolymer | FERREX® |
| ExxonMobil™ PP6272NE1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |