Hostacom TKC 782N
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BhzHtY_Hostacom-TKC-782N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom TKC 782N high melt flow, 1,200 MPa flexural modulus, natural, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent combination of properties and processability. It was designed for automotive interior components that require balanced impact and stiffness characteristics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 16.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 12 | % | ISO 527-2 |
| Flexural Modulus | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 53 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 82.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205.3 TFE 5 | RTP Company | Nylon 66 | RTP |
| Shin-Etsu Elastomer FEA-251U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| Visico™ LE4423/LE4437 | Borealis AG | XLPE | Visico™ |
| EPAMOULD 665A76 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| ULTEM™ CRS5201 resin | SABIC Innovative Plastics | PEI | ULTEM™ |