NORYL™ WCV072 resin
| Category: | PPE+PS+PP , Polyphenylene Ether + PS + PP |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bhuo8i_NORYL-WCV072-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. Designed for evaluation in applications requiring ISO6722. 72 Shore D hardness. Processed using standard extrusion equipment. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 13.4 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.12 | % | |
| Equilibrium, 23°C, 50% RH | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1710 | MPa | ASTM D638 |
| -- | 1760 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.8 | MPa | ASTM D638 |
| Yield | 44.6 | MPa | ISO 527-2/50 |
| Break 3 | 41.5 | MPa | ASTM D638 |
| Break | 42.1 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 15 | % | ASTM D638 |
| Yield | 11 | % | ISO 527-2/50 |
| Break 5 | 83 | % | ASTM D638 |
| Break | 46 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1560 | MPa | ASTM D790 |
| -- 7 | 1750 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 59.3 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 53.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 34 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 67 | J/m | ASTM D256 |
| 23°C | 310 | J/m | ASTM D256 |
| -30°C 10 | 6.9 | kJ/m² | ISO 180/1A |
| 23°C 11 | 37 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 45.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 92.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 98.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 114 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 117 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 8.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultralloy™ 109 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Abstron IM17A DLW | Bhansali Engineering Polymers Limited | ABS | Abstron |
| APEX® 3703-92NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Clariant Acetal CP-MF5 | Clariant Corporation | Acetal (POM) Copolymer | Clariant Acetal |
| LNP™ THERMOCOMP™ RF007SXN compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |