SABIC® HDPE F01552
| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bgx1QS_SABIC-HDPE-F01552.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC®HDPE F01552 is a high density (MMW) polyethylene product,. It can be processed by blowing film and is available in Europe. SABIC®The application areas of HDPE F01552 include bags/linings and movies. The main characteristics are: accessible food. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.15 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 16 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 15 µm | 1400 | MPa | ASTM D882 |
| TD : 15 µm | 1700 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 15 µm | 31.0 | MPa | ASTM D882 |
| TD : Yield, 15 µm | 30.0 | MPa | ASTM D882 |
| MD : Break, 15 µm | 55.0 | MPa | ASTM D882 |
| TD : Break, 15 µm | 49.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 15 µm | 400 | % | ASTM D882 |
| TD : Break, 15 µm | 610 | % | ASTM D882 |
| Dart Drop Impact | 180 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 4.0 | g | ASTM D1922 |
| TD | 40 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Additional Information |
|---|
| Properties determined on 15 µm blown film with a blow up ratio of 1:4. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 235 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 GV 10 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| TRIBOCOMP® POM TS0 | EPIC Polymers | Acetal (POM) Copolymer | TRIBOCOMP® |
| APEX® 1525 | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina WHITE PVC COMPOUND 550-10/10-IS-SD-AS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Rotuba CAB B9024 (7% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |