POLYfill PP HJ752 UV2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bgwhb0_POLYfill-PP-HJ752-UV2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP/Elastomer Mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 to 1.0 | % | |
| Flow | 0.80 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 22.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 1900 | MPa | ISO 178 |
| Flexural Stress | 32.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 113 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| CLTE - Flow | 5.5E-5 to 6.5E-5 | cm/cm/°C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 86002-85FUV Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen EP240P | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Adell PP EQ-16 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| Fainplast PVC PM 64/OP | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| ISPLEN® PG 370 AT | REPSOL | PP Homopolymer | ISPLEN® |