Monprene® OM-10240
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BgQDGt_Monprene-OM-10240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Monprene®OM-10240 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Monprene®The main features of the OM-10240 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 1 sec | 35 | ASTM D2240 | |
| Shore A, 1 second, injection molding 1 | 43 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding 2 | 40 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 3 | 1.48 | MPa | ASTM D412 |
| Flow : 100% strain 4 | 1.61 | MPa | ASTM D412 |
| Transverse flow : 300% strain 5 | 3.16 | MPa | ASTM D412 |
| Flow : 300% strain 6 | 3.41 | MPa | ASTM D412 |
| Tensile Strength 7 | ASTM D412 | ||
| Transverse flow : Fracture | 5.18 | MPa | ASTM D412 |
| Flow : Fracture | 4.83 | MPa | ASTM D412 |
| Tensile Elongation 8 | ASTM D412 | ||
| Transverse flow : Fracture | 470 | % | ASTM D412 |
| Flow : Fracture | 450 | % | ASTM D412 |
| Tear Strength 9 | ASTM D624 | ||
| Transverse flow | 21.9 | kN/m | ASTM D624 |
| Flow | 21.4 | kN/m | ASTM D624 |
| Compression Set 10 | ASTM D395B | ||
| 23°C, 22 hr | 39 | % | ASTM D395B |
| 70°C, 22 hr | 80 | % | ASTM D395B |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 138 - 160 | °C | |
| Middle Temperature | 182 - 199 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 193 - 210 | °C | |
| Processing (Melt) Temp | 177 - 199 | °C | |
| Mold Temperature | 4.44 - 32.2 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 潮湿会使材料降解。建议进行干燥处理。可以把材料放入除湿干燥机，在140°F的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 138 - 149 | °C | |
| Cylinder Zone 2 Temp. | 149 - 160 | °C | |
| Cylinder Zone 3 Temp. | 160 - 182 | °C | |
| Cylinder Zone 5 Temp. | 171 - 193 | °C | |
| Die Temperature | 182 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | Aging 48 hr |
| 2 . | Aging 48 hr |
| 3 . | Mouth die C, 510mm/min |
| 4 . | Mouth die C, 510mm/min |
| 5 . | C mold, 510mm/min |
| 6 . | C mold, 510mm/min |
| 7 . | C mold, 510mm/min |
| 8 . | Mouth die C, 510mm/min |
| 9 . | C mold, 510mm/min |
| 10 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA6 33 GF BLK | RTP Company | Nylon 6 | RTP |
| RAMOFIN PPC364I6 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| AMTOPP CI20 | Inteplast Group | PP, Unspecified | AMTOPP |
| Devcon HV Tile Adhesive | Devcon | Epoxy | Devcon |
| Kazan LDPE 16214-020 OKP 22 111 3403 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |