Generic Nylon 66 - Proprietary
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bg3zKu_Generic-Nylon-66---Proprietary.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Proprietary This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 - 2.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.29 - 2.0 | % | ASTM D955 |
| Transverse flow : 23°C | 0.75 - 2.1 | % | ASTM D955 |
| 23°C | 0.79 - 1.5 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.30 - 1.1 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 - 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3140 - 15600 | MPa | ASTM D638 |
| 23°C | 3180 - 14100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Fracture, 23°C | 71.7 - 206 | MPa | ASTM D638 |
| Fracture, 23°C | 70.0 - 200 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 2.1 - 9.2 | % | ISO 527-2 |
| Fracture, 23°C | 1.4 - 21 | % | ASTM D638 |
| Fracture, 23°C | 1.8 - 6.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2760 - 12200 | MPa | ASTM D790 |
| 23°C | 2800 - 11600 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 96.0 - 268 | MPa | ISO 178 |
| Fracture, 23°C | 221 - 413 | MPa | ASTM D790 |
| Coefficient of Friction | 0.34 - 0.82 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 - 43 | J/m | ASTM D256 |
| 23°C | 3.9 - 5.1 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 420 - 1900 | J/m | ASTM D256 |
| 23°C | 28 - 250 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 3.80 - 29.1 | J | ASTM D3763 |
| 23°C | 0.780 - 3.14 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 184 - 262 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 156 - 260 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 236 - 255 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 62.0 - 253 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 8.5E-6 - 6.3E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 7.6E-5 - 7.8E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 271 - 272 | °C | |
| Middle Temperature | 288 | °C | |
| Front Temperature | 299 | °C | |
| Processing (Melt) Temp | 282 - 293 | °C | |
| Mold Temperature | 87.8 - 102 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - ProprietaryThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starglas GX05052 | Eurostar Engineering Plastics | PSU | Starglas |
| Tarflen® SM-S15G2 | Grupa Azoty S.A. | PTFE | Tarflen® |
| Delta N66-1800 HSL | Delta Polymers | Nylon 66 | Delta |
| DURANEX® CRN7030GP | Polyplastics Co., Ltd. | PBT | DURANEX® |
| K-Prene INSULATION EPR 5082 | Technovinyl Polymers India Ltd. | MPR | K-Prene |