Novalloy-B B27B3 (Type M)
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bfwa61_Novalloy-B-B27B3-Type-M-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-B B27B3 (Type M) is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) material filled with 15% glass fiber. It is available in Asia Pacific. Primary attribute of Novalloy-B B27B3 (Type M): Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 80.0 | MPa | ISO 527-2 |
| Flexural Modulus | 5000 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 200 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 180 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 155 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 1.0E-4 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Back Pressure | 5.00 to 20.0 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resirene 7600 | Resirene, S.A. de C.V. | PS (HIPS) | Resirene |
| Moplen HP500H | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Bakelite® PF 7596 | Hexion Inc. | Phenolic | Bakelite® |
| Fainplast PVC GS 55/AT | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LEXAN™ BFL4000U resin | SABIC Innovative Plastics | PC | LEXAN™ |