Ebalta SG 130 / PUR 11
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bf01ie_Ebalta-SG-130-PUR-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This is a Polyurethane system. Material should be carefully stirred up/shaked before use. Filler content and sales units are on the separate mixing table noted. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 to 74 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 900 to 1100 | MPa | ISO 178 |
| Flexural Stress | 55.0 to 65.0 | MPa | ISO 178 |
| Compressive Stress | 42.0 to 52.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 24 to 29 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 81.0 to 87.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.08 to 1.12 | g/cm³ | |
| Viscosity (25°C) | 0.055 to 0.095 | Pa·s | |
| Curing Time (20°C) | 0.50 to 1.5 | hr | |
| Pot Life 1(20°C) | 2.5 to 3.5 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Formolon® 172 | Formosa Plastics Corporation, U.S.A. | PVC Alloy | Formolon® |
| DynaChar™ XP-2235 | Polymer Dynamix | TPU, Unspecified | DynaChar™ |
| GAPEX® APP40GL03WH | Ferro Corporation | PP Homopolymer | GAPEX® |
| Latimass 52/11-04 D008 | LATI S.p.A. | PP Homopolymer | Latimass |
| Petlon R-Prime A3-G15-00-BK | Petlon Polymers Ltd | Nylon 66 | Petlon R-Prime |