Desmopan® DP 2587 A
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BeZpZQ_Desmopan-DP-2587-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; does not contain any anti-hydrolysis agent; Application; Blown films |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 23°C | 86 | ||
| Shore D, 23°C | 33 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | DIN 53504 | ||
| Break, 23°C | 47.6 | MPa | |
| 10% Strain, 23°C | 2.50 | MPa | |
| 50% Strain, 23°C | 5.30 | MPa | |
| 100% Strain, 23°C | 6.70 | MPa | |
| 300% Strain, 23°C | 22.4 | MPa | |
| Tensile Strain 2(Break, 23°C) | 480 | % | DIN 53504 |
| Abrasion Resistance | 30.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 41.0 | MPa | |
| 20°C | 12.0 | MPa | |
| 60°C | 7.70 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 40 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3(23°C) | 70 | kN/m | ISO 34-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Melt Temperature | 195 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | 200 mm/min |
| 2 . | 200 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moldex® QS981A/M151 | Mitsubishi Chemical Corporation | Polyolefin, Unspecified | Moldex® |
| Formolene® L62009X | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| LNP™ STAT-LOY™ AF3009 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |
| LNP™ LUBRICOMP™ DL003P compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| HIVOREX FL7100 | Lotte Chemical Corporation | HDPE | HIVOREX |