Order Products : sales@su-jiao.com
GAZOLE™ 5200P
| Category: | PBI , Polybenzimidazole |
| Manufacturer: | Gharda Chemicals Ltd. |
| Trademark: | GAZOLE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BeAuGH_GAZOLE-5200P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Details: Ultra High performance thermoplastic polymer, unreinforced PBI Poly (2, 5 benzimidazole), semi crystalline, fine powder for compression molding, standard particle size distribution, color natural brown. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | |
| Apparent Density | 0.15 | g/cm³ | ASTM D1895B |
| Moisture Content - GSRF | 2.0 to 3.0 | % | |
| Particle Size Distribution - D(100) | < 130.0 | µm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weight Loss on Heating | Internal Method | ||
| 5% Weight Loss in Air | 570 | °C | |
| 5% Weight Loss in Nitrogen | 520 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 125 | ASTM D785 | |
| Durometer Hardness (Shore D) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5900 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 160 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 220 | MPa | ASTM D790 |
| Compressive Modulus | 5900 | MPa | ASTM D695 |
| Compressive Strength | 390 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 440 | °C | ASTM D648 |
| Continuous Use Temperature | 400 | °C | UL 746B |
| Glass Transition Temperature | 467 | °C | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm) | 23 | kV/mm | ASTM D149 |
| Arc Resistance 1 | 185 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr |
| Note Message | |
|---|---|
| 1 . | @500 Volts |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 5061R 65308 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| ACCUCOMP™ ABS811L | ACLO Compounders Inc. | ABS | ACCUCOMP™ |
| ExxonMobil™ LLDPE LL 3402.48 Blown | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Edgetek™ SF-40GF/000 RS BK001 | PolyOne Corporation | PPS | Edgetek™ |
| Hylon® N1043STL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |