Generic Nylon 6 - Glass Bead
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BdkVgl_Generic-Nylon-6---Glass-Bead.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Glass Bead This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.26 - 1.38 | g/cm³ | ASTM D792 |
| 23°C | 1.33 - 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.45 - 1.7 | % | ASTM D955 |
| 23°C | 0.47 - 1.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.75 - 1.4 | % | ASTM D570 |
| 23°C, 24 hr | 1.0 - 7.0 | % | ISO 62 |
| Saturated, 23°C | 6.5 - 6.7 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 - 2.1 | % | ISO 62 |
| Viscosity Number | 145 - 150 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 95 - 120 | ASTM D785 | |
| Durometer Hardness (23°C) | 85 | ISO 868 | |
| Ball Indentation Hardness | 172 - 203 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4090 - 6000 | MPa | ASTM D638 |
| 23°C | 2900 - 6200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 50.0 - 100 | MPa | ASTM D638 |
| Yield, 23°C | 40.0 - 103 | MPa | ISO 527-2 |
| Fracture, 23°C | 59.9 - 80.5 | MPa | ASTM D638 |
| Fracture, 23°C | 53.1 - 116 | MPa | ISO 527-2 |
| 23°C | 69.8 - 103 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 1.6 - 20 | % | ISO 527-2 |
| Fracture, 23°C | 1.7 - 13 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 11 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3170 - 4570 | MPa | ASTM D790 |
| 23°C | 2630 - 5250 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 99.5 - 162 | MPa | ASTM D790 |
| 23°C | 77.6 - 160 | MPa | ISO 178 |
| Fracture, 23°C | 99.0 - 142 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 - 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 17 - 60 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 29 - 75 | J/m | ASTM D256 |
| 23°C | 3.0 - 6.2 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 200 - 550 | J/m | ASTM D256 |
| 23°C | 25 - 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 188 - 202 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 167 - 217 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 69.6 - 201 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 60.0 - 203 | °C | ISO 75-2/A |
| Continuous Use Temperature | 80.0 - 160 | °C | ASTM D794 |
| Vicat Softening Temperature | 198 - 206 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 215 - 223 | °C | |
| -- | 218 - 222 | °C | ISO 11357-3 |
| -- | 218 - 219 | °C | ASTM D3418 |
| -- | 220 - 222 | °C | ISO 3146 |
| Linear thermal expansion coefficient | |||
| Flow | 4.5E-5 - 6.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.4E-5 - 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.9E-5 - 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+8 - 2.5E+14 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+14 - 6.1E+15 | ohms·cm | ASTM D257 |
| 23°C | 11 - 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 14 - 21 | kV/mm | ASTM D149 |
| 23°C | 10 - 36 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 3.75 | IEC 60250 | |
| Dissipation Factor (23°C) | 0.020 | IEC 60250 | |
| Comparative Tracking Index | 443 - 556 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 642 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 22 - 24 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.8 - 90.3 | °C | |
| Drying Time | 2.0 - 11 | hr | |
| Suggested Max Moisture | 0.089 - 0.25 | % | |
| Suggested Max Regrind | 15 | % | |
| Rear Temperature | 239 - 282 | °C | |
| Middle Temperature | 246 - 282 | °C | |
| Front Temperature | 246 - 283 | °C | |
| Processing (Melt) Temp | 256 - 281 | °C | |
| Mold Temperature | 69.4 - 100 | °C | |
| Injection Pressure | 70.8 - 95.1 | MPa | |
| Holding Pressure | 42.8 - 60.2 | MPa | |
| Back Pressure | 0.172 - 0.525 | MPa | |
| Screw Speed | 45 - 125 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Glass BeadThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ 403/450 BK | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| TPX® MX004XB | Mitsui Chemicals, Inc. | PMP Copolymer | TPX® |
| NORYL GTX™ GTX840 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| Colorite 12 Series 7012 | Colorite Polymers | PVC, Unspecified | Colorite 12 Series |
| EcoVid 43TFH | Greener Polymers Inc. | PLA | EcoVid |