Wellamid® GS25-66 22LH-NBK1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bcr4lz_Wellamid-GS25-66-22LH-NBK1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wellamid® GS25-66 22LH-NBK1 is a Polyamide 66 (Nylon 66) material filled with 25% glass bead. It is available in Asia Pacific, Europe, Latin America, or North America. Primary attribute of Wellamid® GS25-66 22LH-NBK1: Flame Rated. Typical application of Wellamid® GS25-66 22LH-NBK1: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.6 to 2.0 | % | |
| Flow | 1.4 to 1.8 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 112 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 2.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 84.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNAMID® A A-SV30-TAP | Poly Plastic | Nylon 66 | TECHNAMID® A |
| Unichem 40-105 | Colorite Polymers | PVC, Unspecified | Unichem |
| ExxonMobil™ PP2822E1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Estane® 2103-80AEN TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Iupilon® EGN2010R2 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |