EPO-TEK® 930-4
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bcpt3L_EPO-TEK-930-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® 930-4 is a two component, thermally conductive epoxy, formulated with a very fine boron-nitride filler particle. Also available in a single component frozen syringe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 425 | °C | TGA |
| Die Shear Strength - >15 kg (23°C) | 35.2 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 325 | °C | |
| Storage Modulus (23°C) | 4.19 | GPa | |
| Thixotropic Index | 2.40 | ||
| Weight Loss on Heating | |||
| 200°C | 0.10 | % | |
| 250°C | 0.33 | % | |
| 300°C | 0.73 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 90.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 2.7E-5 | cm/cm/°C | |
| -- 3 | 1.4E-4 | cm/cm/°C | |
| Thermal Conductivity | 1.7 | W/m/K |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 3.3 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 4 | Amber | ||
| -- 5 | Ivory | ||
| Density | |||
| Part B | 1.02 | g/cm³ | |
| Part A | 1.31 | g/cm³ | |
| Viscosity 6(23°C) | 12 to 17 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 1400 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 | ||
| Lap Shear Strength (23°C) | > 13.3 | MPa | |
| Relative Permittivity (1 kHz, 23°C) | 3.73 | ||
| Volume Resistivity (23°C) | > 2.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz, 23°C) | 4.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rynite® GW520CS NC010 | DuPont Performance Polymers | PET | Rynite® |
| TEKALOY™ G70NH | Mando Advanced Materials Co., Ltd. | PC+ABS | TEKALOY™ |
| THERMOLAST® K TC8SCE (Series: SCR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| K-Resin® SBC BK10 | Chevron Phillips Chemical Company LLC | SBC | K-Resin® SBC |
| Sylvin 916VO Grey 9154 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |