Elastollan® 1195 A
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BcWt3v_Elastollan-1195-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermoplastic Polyether Polyurethane Elastomers with outstanding hydrolysis resistance, low temperature flexibility and resistance to micro-organisms. Typical applications Cable jackets, plugs and terminations, spiral tubing, Films, ski-boot shells, ear tags, technical mouldings like mining screens, railway pads, seals. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 7619 | ||
| Shore A, 3 sec | 96 | ||
| Shore D, 3 sec | 48 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504 | ||
| 20% Strain | 6.00 | MPa | |
| 100% Strain | 10.0 | MPa | |
| 300% Strain | 18.0 | MPa | |
| Tensile Stress | DIN 53504 | ||
| Yield 1 | 37.0 | MPa | |
| Yield | 55.0 | MPa | |
| Tensile Elongation 2(Break) | 500 | % | DIN 53504 |
| Tear Strength 3 | 100 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 30 | % | |
| 70°C, 24 hr | 45 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 170 to 240 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | after storage in water at 80°C for 42 days |
| 2 . | after storage in water at 80°C for 42 days |
| 3 . | Method Bb, Angle (Nicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V955 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| XANTAR® LDS 3760 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® LDS |
| LONOY lonoy 1600 | Kingfa | PC+PBT | LONOY |
| LEXAN™ EXL5689 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| ULTEM™ 2100 resin | SABIC Innovative Plastics | PEI | ULTEM™ |