AURAPENE PPHUFNAT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Aurora Manufacturing Ltd |
| Trademark: | AURAPENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BZAb78_AURAPENE-PPHUFNAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPUFNATX is a general purpose Homopolymer polypropylene compound manufactured from recycled polymer. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.904 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 to 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.3 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strain (Break) | 16 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | > 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 152 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 1 | < 100 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Rear Temperature | 195 to 230 | °C | |
| Middle Temperature | 195 to 230 | °C | |
| Front Temperature | 195 to 230 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4065 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Axiall PVC 8150 White 119 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| LNP™ THERMOCOMP™ RF002ES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Zytel® FR70G25GWNH WT409 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| PONACOM PS 5570-10 | Ponachem Compound GmbH | PS (HIPS) | PONACOM PS |