SLOVAMID® 6 GF 30 HTS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BYhomQ_SLOVAMID-6-GF-30-HTS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6 for injection moulding, chemically reinforced with 30% glass fibre, heat stabilized, mouldings resistant against longtime heat impact up to 170°C, resistive against hydrolysis. Used in environment, where long-time temperatures up to 200°C occur. Decrease in tensile strength by 50% after 5000 hours at 170°C. Application: grips of electrotools, hobby tools, gears, covers of electric appliances. Heat stabilization predetermines these prodcts to an environment with longtime heat stress like eg.: intake piping, cylinder heads, induction coils, carrying parts in the motor fixing in the motor area. Delivered in black colour. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.5 | % | |
| Flow | 0.58 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 10 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 45 | kJ/m² | |
| 23°C | 55 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 200 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 210 | °C | ISO 306/B |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 8.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 5.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 20 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 575 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2404H4 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Shin-Etsu RTV KE-441 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| UBESTA XPA 9063 X1 | UBE Engineering Plastics, S.A. | Nylon 12 Elast | UBESTA |
| Elastron® G G100.A70.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Axiall PVC GP-9190 | Axiall Corporation | PVC, Rigid | Axiall PVC |