NORYL™ N1150 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BY42SL_NORYLN1150resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL N1150 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 0.75 mm with a specific density of 1.11 g/cm^3. NORYL 1150 may be an excellent material candidate for applications requiring electrically insulating properties, low moisture absorption, low warpage, and thin wall flame resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption (Saturation, 23°C) | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2700 | MPa | ASTM D638 |
| -- | 2650 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 75.0 | MPa | ASTM D638 |
| Yield | 72.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 55.0 | MPa | ASTM D638 |
| Fracture | 52.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Yield | 3.5 | % | ISO 527-2/50 |
| Fracture 5 | 8.0 | % | ASTM D638 |
| Fracture | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3050 | MPa | ASTM D790 |
| -- 7 | 2600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 105 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 65 | J/m | ASTM D256 |
| 23°C | 85 | J/m | ASTM D256 |
| -30°C 10 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 40.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 108 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 109 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ASTM D1525, ISO 306/B50 11 13 |
| -- | 132 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 5.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 5.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 5.0E+16 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Constant (1 MHz) | 2.60 | ASTM D150, IEC 60250 | |
| Dissipation Factor (1 MHz) | 3.0E-3 | ASTM D150, IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 2.50 mm | 5VA | UL 94 | |
| Oxygen Index | 38 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 98.9 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 227 - 277 | °C | |
| Middle Temperature | 238 - 282 | °C | |
| Front Temperature | 249 - 288 | °C | |
| Nozzle Temperature | 260 - 288 | °C | |
| Processing (Melt) Temp | 260 - 288 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProPell™ TPU 55D 0118A | Foster Corporation | Unspecified | ProPell™ |
| Sumikon® FM-MK115S | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| EVICOM™ RG7/295H | INEOS Compounds | PVC, Flexible | EVICOM™ |
| Edgetek™ PK-30CF/000 BK | PolyOne Corporation | PEEK | Edgetek™ |
| Sylvin 4200-85 Green 3212 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |