POLYNIL® P75
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | POLYNIL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BY3QW4_POLYNIL-P75.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYNIL® P75 is an unreiforced Polyamide 66 (Nylon 66) for extrusion. This 3.1 viscosity Polyamide 66 resin is FDA compliant and is NSF-61 certified for contact with potable water. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | |
| Saturation, 23°C | 8.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 82.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 85 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 72.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 85.0 | °C | IEC 60216 |
| Vicat Softening Temperature | 240 | °C | ISO 306/B |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass | ||
| Melting Temperature | 258 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 750 | °C | |
| 3.20 mm | 850 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 775 | °C | |
| 3.20 mm | 750 | °C | |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 10.NB | Marco Polo International, Inc. | PP Copolymer | MARPOL® COPP |
| AKROMID® B3 GF 60 1 black (2489) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| CALP MRP430 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| ELASTOSIL® LR 3003/70 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| HyTemp® AR71L | Zeon Chemicals L.P. | Acrylic, Unspecified | HyTemp® |