ASTAMID™ MB3M6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BXYSwc_ASTAMID-MB3M6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAMID™ MB3M6 is a 30% Mineral filled PA6. This grade is recommended for applications requiring good dimensional stability/ low warpage such as wheels and engine covers. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 0.70 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 2(3.20 mm) | 4600 | 1650 | MPa | ASTM D638 |
| Tensile Strength 3(3.20 mm) | 80.0 | -- | MPa | ASTM D638 |
| Tensile Elongation 4(Break, 3.20 mm) | 4.0 | -- | % | ASTM D638 |
| Flexural Modulus 5(3.20 mm) | 4000 | 1400 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 6 | 9.0 | 24 | kJ/m² | ISO 179 |
| Notched Izod Impact (3.20 mm) | 50 | 130 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, unannealed, 3.20mm | 195 | -- | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 65.0 | -- | °C | ASTM D648 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 260 - 270 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Processing (Melt) Temp | 270 - 280 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Injection Pressure | 80.0 - 130 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 5.0 - 9.0 | kN/cm² |
| Injection instructions |
|---|
| Drying Time (Opened Bag): >12 hr |
| Note Message | |
|---|---|
| 1 . | Constrained |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 10x4.0 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8347-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TPUCO® TPU-CH85 | Taiwan PU Corporation | TPU-Polyether | TPUCO® |
| NuSil MED-6600 | NuSil Technology | Silicone | NuSil |
| Fusabond® N493 | DuPont Packaging & Industrial Polymers | Ethylene Copolymer | Fusabond® |
| ESENTTIA 01R25 | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |