LUVOCOM® 1800-8480 Datasheet,PET,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1800-8480 is a polyethylene terephthalate (PET) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1800-8480 are: Wear-resistant Lubrication Typical application areas include: textile/fiber engineering/industrial accessories Automotive Industry business/office supplies

General Information
Additive	PTFE lubricant
Features	Low friction coefficient Good wear resistance Lubrication
Uses	Textile applications Engineering accessories Application in Automobile Field Business equipment
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.42	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (280°C/1.2 kg)	18.0	cm³/10min	ISO 1133
Molding Shrinkage	1.5 - 2.0	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.30	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2600	MPa	ISO 527-2
Tensile Stress (Break)	49.0	MPa	ISO 527-2
Tensile Strain (Yield)	2.8	%	ISO 527-2
Flexural Modulus	2200	MPa	ISO 178
Flexural Stress	70.0	MPa	ISO 178
Coefficient of Friction
Dynamic	0.18
Static	0.11
Flexural Strain at Flexural Strength	3.2	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	180	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	29	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	100	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+12	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
B	80.0	°C
Hot air dryer, A	120	°C
Drying Time
B	6.0 - 8.0	hr
Hot air dryer, A	2.0 - 5.0	hr
Suggested Max Moisture	0.020	%
Rear Temperature	285 - 295	°C
Middle Temperature	270 - 280	°C
Front Temperature	265 - 275	°C
Nozzle Temperature	265 - 275	°C
Processing (Melt) Temp	280	°C
Mold Temperature	60.0 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 300°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 300°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	BWuBMA_LUVOCOM-1800-8480.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Vi-Chem PVC VNC75I	Vi-Chem Corporation	PVC, Unspecified	Vi-Chem PVC
Alcryn® 2170 NC	Advanced Polymer Alloys	MPR	Alcryn®
CERTENE™ LLGF-120A	Muehlstein	LLDPE	CERTENE™
Kepital® TP-20	Korea Engineering Plastics Co., Ltd	Acetal (POM) Copolymer	Kepital®
Hostacom DB273A	LyondellBasell Industries	TPO (POE)	Hostacom