NORYL GTX™ GTX902 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BVdTu0_NORYLGTXGTX902resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced. Excellent chemical resistance and paintability. 312F (155C) HDT. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 130°C, 1 hour | 1.1 - 1.5 | % | ASTM D955 |
| Flow : 3.20mm | 0.90 - 1.2 | % | Internal method |
| Transverse flow : 3.20mm | 0.80 - 1.1 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C | 3.6 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 60.0 | MPa | ASTM D638 |
| Fracture | 56.5 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 9.0 | % | ASTM D638 |
| Fracture | 52 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 2240 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 100 mm Span) | 89.6 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 19.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 53 | J/m | ASTM D256 |
| -30°C | 120 | J/m | ASTM D256 |
| 23°C | 270 | J/m | ASTM D256 |
| Unnotched Izod Impact | ASTM D4812 | ||
| -40°C | 3200 | J/m | ASTM D4812 |
| -30°C | 3200 | J/m | ASTM D4812 |
| 23°C | 3200 | J/m | ASTM D4812 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Energy at Peak Load | 19.7 | J | ASTM D3763 |
| -30°C, Energy at Peak Load | 36.0 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 46.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 156 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 128 | °C | ASTM D648 |
| Vicat Softening Temperature | 233 | °C | ASTM D1525 5 |
| CLTE - Flow (-20 to 150°C) | 9.0E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 260 - 299 | °C | |
| Middle Temperature | 266 - 299 | °C | |
| Front Temperature | 271 - 299 | °C | |
| Nozzle Temperature | 277 - 299 | °C | |
| Processing (Melt) Temp | 277 - 299 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michilene F8100GC20-01 | API Polymers, Inc. | PP Homopolymer | Michilene |
| Nanjing Hongrui PBT T303 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| Generic HDPE, HMW | Generic | HDPE, HMW | Generic |
| elitel UE3231 | UNITIKA Plastics Division | TPC-ET | elitel |
| ENVIROPLAS® ENV08-NC460 | ENVIROPLAS®, Inc. | PBT | ENVIROPLAS® |