INEOS PP L70J-00
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BVIGHv_INEOS-PP-L70J-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| L70J-00 is a high melt flow rate, nucleated, lightly antistated impact copolymer polypropylene designed for high stiffness, thin-walled containers having a high length-to-thickness ratio (L/T). This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.910 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 70 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 28.4 | MPa | |
| Break | 16.6 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 4.9 | % | |
| Break | 38 | % | |
| Flexural Modulus - 1% Secant | 1550 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 33 | J/m | |
| 23°C | 65 | J/m | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C | 3.20 | kJ/m² | |
| 23°C | 6.40 | kJ/m² | |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Brittle | ||
| 23°C | Mixed |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 120 | °C | |
| 1.8 MPa, Unannealed | 57.8 | °C | |
| Vicat Softening Temperature | 151 | °C | ASTM D1525 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 66 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miraprene® QS2215 | Mitsubishi Chemical Corporation | TPO (POE) | Miraprene® |
| GERMAMID 6.6 CU 80 HY | Kunststoff-Kontor-Hamburg GmbH | Nylon 66 | GERMAMID |
| Hostacom HKC 182L C11504 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Durez® 33751 | SBHPP | Phenolic | Durez® |
| LNP™ THERMOTUF™ OX96685 compound | SABIC Innovative Plastics | PPS | LNP™ THERMOTUF™ |