Skyrol® SP91
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SKC Inc. |
| Trademark: | Skyrol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BUfLl9_Skyrol-SP91.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Skyrol® SP91 is a one side chemically treated polyester film which provides enhanced adhesion to various kinds of metals, inks, and adhesives. When metallized on the chemically pretreated surface, SP91 shows significantly improved adhesion characteristics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.40 | g/cm³ | ASTM D1505 |
| Molding Shrinkage | Internal Method | ||
| Flow : 150°C, 30 min, 0.0120 mm | 1.7 | % | |
| Flow : 150°C, 30 min, 0.0230 mm | 1.6 | % | |
| Across Flow : 150°C, 30 min, 0.0120 mm | 0.80 | % | |
| Across Flow : 150°C, 30 min, 0.0230 mm | 1.2 | % | |
| Surface Tension - Treated | |||
| 12.0 µm | 55 | mN/m | ASTM D257 |
| 23.0 µm | 55 | mN/m | ASTM D2578 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 2 | 0.30 | ||
| vs. Itself - Dynamic 3 | 0.40 | ||
| vs. Itself - Static 4 | 0.40 | ||
| vs. Itself - Static 5 | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 12 µm | 290 | MPa | |
| MD : Yield, 23 µm | 276 | MPa | |
| TD : Yield, 12 µm | 255 | MPa | |
| TD : Yield, 23 µm | 248 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 12 µm | 120 | % | |
| MD : Break, 23 µm | 130 | % | |
| TD : Break, 12 µm | 120 | % | |
| TD : Break, 23 µm | 120 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 12.0 µm | 164 | ||
| 23.0 µm | 163 | ||
| Transmittance | ASTM D1003 | ||
| 12.0 µm | 90.0 | % | |
| 23.0 µm | 90.0 | % | |
| Haze | ASTM D1003 | ||
| 12.0 µm | 3.0 | % | |
| 23.0 µm | 4.0 | % |
| Note Message | |
|---|---|
| 1 . | 23 µm |
| 2 . | 23 µm |
| 3 . | 12 µm |
| 4 . | 12 µm |
| 5 . | 23 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2100TN21 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Baoding 76E90 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| Lifoflex® UV FLAM 80600 | Müller Kunststoffe GmbH | TPE | Lifoflex® |
| LNP™ STAT-KON™ EX01696C compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| Polychim HB12XF | Polychim Industrie S.A.S. | PP Homopolymer | Polychim |