TOTAL Polypropylene PPH 4026
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BUeoHB_TOTAL-Polypropylene-PPH-4026.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPH 4026 is a homopolymer with a Melt Flow Index of 3 g/10 min for the cast extrusion of films with outstanding stiffness and heat resistance. Polypropylene PPH 4026 is intended for applications like hot fill food packaging, labeling, twist or lamination films. Polypropylene PPH 4026 is a polypropylene homopolymer specifically developed to offer outstanding process ability for sheet extrusion and thermoforming applications. Polypropylene PPH 4026 is characterized by a higher stiffness than conventional nucleated homopolymers, a good impact resistance and an excellent clarity. Polypropylene PPH 4026 allows for wall thickness reduction while maintaining appropriate top load and crush resistances. Polypropylene PPH 4026 has excellent organoleptic properties making it suitable for the most sensitive packaging application. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2050 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 39.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, Cast Film | 31.0 | MPa | |
| TD : Yield, 50 µm, Cast Film | 29.0 | MPa | |
| MD : Break, 50 µm, Cast Film | 62.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 35.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 470 | % | |
| TD : Break, 50 µm, Cast Film | 580 | % | |
| Dart Drop Impact (50 µm, Cast Film) | 80 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 6.0 | kN/m | |
| TD : 50.0 µm | 88.0 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A50 |
| -- | 97.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 51 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 14 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 C 15 MI | Plastcom | Nylon 66 | SLOVAMID® 66 |
| NEUSoft™ 597 Ether 60 | NEU Specialty Engineered Materials | TPU, Unspecified | NEUSoft™ |
| GAPEX® RPP30EA16NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| EMOPLEN® CP MTF 15 UV | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |
| K-Prene XL-A80 | Technovinyl Polymers India Ltd. | PP+EPDM | K-Prene |