TRIEL® 5450
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | Samyang Corporation |
| Trademark: | TRIEL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BTyqCf_TRIEL-5450.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIEL® 5450 is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in Asia Pacific, Europe, or North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 1.7 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Break | 20.6 | MPa | |
| 5.0% Strain | 5.88 | MPa | |
| 10% Strain | 8.34 | MPa | |
| 50% Strain | 12.7 | MPa | |
| Tensile Elongation (Break) | > 400 | % | ASTM D638 |
| Flexural Modulus | 90.2 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 5.39 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 73.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 161 | °C | ASTM D1525 1 |
| Melting Temperature | 210 | °C | ASTM D2117 |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-2095-60A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| VITAMIDE® AS30BK6328 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| AIE PA66 60G3 | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| ELASTOSIL® AUX MOULD RELEASE A | Wacker Chemie AG | Silicone | ELASTOSIL® AUX |
| CYCOLAC™ INP630 resin | SABIC Innovative Plastics | ABS+SAN | CYCOLAC™ |