WINTEC™ WFX4M
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Japan Polychem Corporation |
| Trademark: | WINTEC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BT7qIy_WINTEC-WFX4M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WINTEC™ WFX4M is a Polypropylene Random Copolymer (PP Random Copolymer) product. It can be processed by injection molding and is available in Asia Pacific. Typical application: Film. |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 7.0 | g/10 min | ISO 1133 |
| Spiral Flow | 46.0 | cm | Internal Method |
| Molding Shrinkage | 1.0 to 1.4 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 75 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 22.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | > 400 | % | ISO 527-2 |
| Flexural Modulus | 750 | MPa | ISO 178 |
| Flexural Stress | 25.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| 0°C | 2.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 70.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 110 | °C | ISO 306 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | 90 | ASTM D523 | |
| Haze | ISO 14782 | ||
| 1000 µm | 15 | % | |
| 2000 µm | 50 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCCPMI40 | Rainmaker Polymers LLC | PP Copolymer | Rainmaker Polypropylene |
| YUPLENE® R140H | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| Buna® EP G 2470 LM | LANXESS Corporation | EPDM | Buna® EP |
| Lucofin® 1414-t2 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| LUVOCOM® 3/XCF/10 | Lehmann & Voss & Co. | Nylon 6 | LUVOCOM® |