SCANAMID 66 A53^EM
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polykemi AB |
| Trademark: | SCANAMID 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BSp2kd_SCANAMID-66-A53-EM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified |
| General Information |
|---|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.8 | -- | % | |
| Flow | 1.6 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | 50.0 | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | 40 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2100 | 1200 | MPa | ISO 178 |
| Flexural Stress | 50.0 | 40.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -20°C | -- | 40 | kJ/m² | |
| 23°C | 50 kJ/m² | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -20°C | -- | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® A1400 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Xuchuan XCW-8955A | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| ALTECH® PA6 A 1000/110 IM | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| ELASTOSIL® R plus 4360/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| LUVOCOM® 20-8112 | Lehmann & Voss & Co. | PPA | LUVOCOM® |