Lumax® GP5306F
| Category: | PBT Alloy , Polybutylene Terephthalate Alloy |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BSPw7L_Lumax-GP5306F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Flame Retardant, General Purpose Applications IT/OA, E&E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 108 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 8140 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 167 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 185 | °C | ASTM D648 |
| Peak Melting Temperature | 223 | °C | ASTM D3418 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 26 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) 5 | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 225 to 235 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 245 to 255 | °C | |
| Nozzle Temperature | 245 to 255 | °C | |
| Processing (Melt) Temp | 245 to 255 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide RF006S-GY9A121 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Sylvin 9302-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 3M™ Dyneon™ PTFE Compound TF 4302 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| ADDILENE H 490 S | ADDIPLAST | PP, Unspecified | ADDILENE |
| APEX® 3601-70 | Teknor Apex Company | PVC, Flexible | APEX® |