Zytel® HTN 51G35HSL NC010
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BRMYLq_Zytel-HTN-51G35HSL-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, PPA, High Performance Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12000 | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 220 | 210 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | 2.2 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 11000 | MPa | |
| 1000 hr | -- | 9500 | MPa | |
| Flexural Modulus | 10500 | 10500 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 11 | -- | kJ/m² | |
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 11 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 45 | kJ/m² | |
| 23°C | 70 | 55 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 11 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 284 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 264 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 300 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 1.8E-5 | -- | cm/cm/°C | |
| Transverse | 5.5E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 5.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 36 | 36 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.00 | -- | ||
| 1 MHz | 4.00 | -- | ||
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.850 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 1860 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.25 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Odor | 4 | -- | VDA 270 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® A1800 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Ferro PP MPP40FJ16BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Karina WHITE PVC COMPOUND -E 837-10/ 68-Y-CRA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Luran® 2580 | Styrolution | SAN | Luran® |
| EPAMOULD 660A26 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |