AMPAL® MPV 7500
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | AMPAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BR5Zd6_AMPAL-MPV-7500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Organically and inorganically filled melamine-modified Polyester moulding compound Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behaviour and wear stability, excellent elasticity Moulded parts in electrical engineering, mainly electromechanical parts like Contact breakers, Relays, Switches, Contact terminals This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 to 1.70 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.90 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | ISO 2577 | ||
| -- 1 | 0.70 to 1.0 | % | |
| -- 2 | 0.90 to 1.2 | % | |
| Water Absorption (23°C, 24 hr) | < 1.4 | % | ISO 62 |
| Post Shrinkage 3 | 0.20 to 0.40 | % | ISO 2577 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | IEC 60216 | ||
| <50 h | 190 | °C | |
| 20,000 h | 140 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 10.0 | MPa | |
| Compression Molding Temperature | 160 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| Compression Molded | 4000 to 6000 | MPa | |
| Injection Molded | 5000 to 7000 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Compression Molded | 30.0 to 50.0 | MPa | |
| Injection Molded | 50.0 to 60.0 | MPa | |
| Flexural Modulus | ISO 178 | ||
| Compression Molded | 6000 to 8000 | MPa | |
| Injection Molded | 6000 to 8000 | MPa | |
| Flexural Stress | ISO 178 | ||
| Compression Molded | 70.0 to 90.0 | MPa | |
| Injection Molded | 90.0 to 110 | MPa | |
| Compressive Stress | 150 to 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| Compression Molded | 2.0 to 3.0 | kJ/m² | |
| Injection Molded | 2.0 to 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| Compression Molded | 10 to 12 | kJ/m² | |
| Injection Molded | 12 to 14 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 180 to 200 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 80.0 to 100 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 2.0E-5 to 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.60 to 0.70 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+11 to 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 30 to 40 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 7.00 5.00 | ||
| 1 MHz | 5.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.10 to 0.20 | ||
| 1 MHz | 0.030 to 0.050 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.40 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 825 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 50.0 to 75.0 | °C | |
| Front Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 100 to 115 | °C | |
| Mold Temperature | 165 to 180 | °C | |
| Back Pressure | 0.800 to 1.20 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | Injection Molded |
| 3 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800B-30D | RTP Company | TPV | RTP |
| Electrafil® PA6/6 CF14 BK | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| Huaxia Shenzhou FKM DS2604-1 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |
| ICORENE® N2170 | ICO Polymers EMEA, A Division of A. Schulman | LDPE | ICORENE® |
| HIFOR Xtreme® SC74871 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |